Medium Weight Winner
We’ve perfected our general purpose medium weight bonding compound a lot over the last 40 years. Today’s 2011 consistently provides a superior bond with less shrinkage and cracking
2011 Bonds Strong and Keeps its Cool
Engineered to provide better resin availability for superior strength in all of your general purpose bonding applications
All medium weight marine bonding compounds are not created equal. That is because many of today’s professional bonding products are “resin-starved”, due to excessive quantities of general filler packing used to regulate viscosity. This may ultimately jeopardize the overall strength and long term durability of the bond, which could inevitably threaten the quality of your project.
Performance Benefits
- Maximum premium resin availability for adhesion
- Low exotherm means less shrinkage & finish work
- Clings to almost any surface, even vertical ones
- Easily pumped through major dispensing equipment
- Provides excellent bond for most general applications
Exotherm & Today's Boat Designs
Because our compound gives off less heat while curing, you get a flexible fill with little or no shrinkage or cracking. This can help save money on finish work - especially with today's intricate hull designs.
2011 in Action
Stays Put
Won't run on almost any surface
Liner to Deck
Preparing to mate a 38' headliner to deck
Filling Strakes
Medium weight used in filling strakes
Availability
| Table Header | REGULAR |
|---|---|
|
2011 Medium Weight Bonding Compound |
|
|
5 Gal Pail | 55 Gal Drum |
RECOMMENDED FOR
| RECOMMENDED FOR | |
|---|---|
|
General Bonding |
General Filling |
|
Liner to Deck |
Filling Strakes |
WORKING PROPERTIES
| GEL TIME | Gel Time | Reaction Time | Fixture Time | Peak Exotherm |
|---|---|---|---|---|
|
45 min |
41 min |
86 min |
180℉ |
TYPICAL PHYSICAL PROPERTIES
| RECOMMENDED FOR | |
|---|---|
|
Color |
White |
|
Odor |
Styrene |
|
Texture |
Smooth |
|
Weight |
9.2 lbs/gallon |
|
Shelf Life |
5 Months, Uncured |
VISCOSITY
| GEL TIME | RPM | µ Min | µ Max |
|---|---|---|---|
|
2 |
900,000 |
1,300,000 |
|
|
20 |
90,000 |
180,000 |
TYPICAL CURED PROPERTIES
| GEL TIME | Test | Average | Deviation |
|---|---|---|---|
|
Tensile Elongation |
2.28% |
1.14% |
|
|
Tensile Strength |
1,490 PSI |
23.5 PSI |
|
|
Compressive Strength |
3,330 PSI |
12.4 PSI |
|
|
Lap Shear |
1,140 PSI |
50 PSI |
|
|
Heat Deflection |
130℉ |
2.5℉ |
|
|
Linear Shrinkage |
<1% |
|
|
|
Shore D Harness |
74-80 |
|